Boosting Magnetoelectric Effect in Polymer-Based Nanocomposites.

Polymer-based magnetoelectric composite materials have attracted a lot of attention due to their high potential in various types of applications as magnetic field sensors, energy harvesting, and biomedical devices. Current researches are focused on the increase in the efficiency of magnetoelectric transformation. In this work, a new strategy of arrangement of clusters of magnetic nanoparticles by an external magnetic field in PVDF and PFVD-TrFE matrixes is proposed to increase the voltage coefficient (αME) of the magnetoelectric effect. Another strategy is the use of 3-component composites through the inclusion of piezoelectric BaTiO3 particles. Developed strategies allow us to increase the αME value from ~5 mV/cm·Oe for the composite of randomly distributed CoFe2O4 nanoparticles in PVDF matrix to ~18.5 mV/cm·Oe for a composite of magnetic particles in PVDF-TrFE matrix with 5%wt of piezoelectric particles. The applicability of such materials as bioactive surface is demonstrated on neural crest stem cell cultures.

Self-Biased Bidomain LiNbO3/Ni/Metglas Magnetoelectric Current Sensor.

The article is devoted to the theoretical and experimental study of a magnetoelectric (ME) current sensor based on a gradient structure. It is known that the use of gradient structures in magnetostrictive-piezoelectric composites makes it possible to create a self-biased structure by replacing an external magnetic field with an internal one, which significantly reduces the weight, power consumption and dimensions of the device. Current sensors based on a gradient bidomain structure LiNbO3 (LN)/Ni/Metglas with the following layer thicknesses: lithium niobate-500 µm, nickel-10 µm, Metglas-29 µm, operate on a linear section of the working characteristic and do not require the bias magnetic field. The main characteristics of a contactless ME current sensor: its current range measures up to 10 A, it has a sensitivity of 0.9 V/A, its current consumption is not more than 2.5 mA, and its linearity is maintained to an accuracy of 99.8%. Some additional advantages of a bidomain lithium niobate-based current sensor are the increased sensitivity of the device due to the use of the bending mode in the electromechanical resonance region and the absence of a lead component in the device.

Dual Vibration and Magnetic Energy Harvesting With Bidomain LiNbO3-Based Composite.

With the recent thriving of low-power electronic microdevices and sensors, the development of components capable of scavenging environmental energy has become imperative. In this article, we studied bidomain congruent LiNbO3 (LN) single crystals combined with magnetic materials for dual, mechanical, and magnetic energy harvesting applications. A simple magneto-mechano-electric composite cantilever, with a trilayered long-bar bidomain LN/spring-steel/metglas structure and a large tip proof permanent magnet, was fabricated. Its vibration and magnetic energy harvesting capabilities were tested while trying to optimize its resonant characteristics, load impedance, and tip proof mass. The vibration measurements yielded a peak open-circuit voltage of 2.42 kV/g, a short-circuit current of [Formula: see text]/g, and an average power of up to 35.6 mW/g2, corresponding to a power density of 6.9 mW/(cm [Formula: see text]), at a low resonance frequency of 29.22 Hz and with an optimal load of 40 [Formula: see text]. The magnetic response revealed a resonant peak open-circuit voltage of 90.9 V/Oe and an average power of up to [Formula: see text]/Oe2, corresponding to a relatively large magnetoelectric coefficient of 1.82 kV/(cm · Oe) and a power density of [Formula: see text]/(cm [Formula: see text]). We thus developed a system that is, in principle, able to scavenge electrical power simultaneously from low-level ambient mechanical and magnetic sources to feed low-power electronic devices.

Low-Frequency Vibration Energy Harvesting With Bidomain LiNbO3 Single Crystals.

Low-frequency vibration energy harvesting is becoming increasingly important for environmentally friendly and biomedical applications in order to power various wearable and implanted devices. In this paper, we propose the use of piezoelectric congruent LiNbO3 (LN) single crystals, with an engineered bidomain structure, as an alternative to the widely employed lead-based PZT. We thus compared experimentally the pure vibration energy scavenging performance of square-shaped bidomain and single-domain Y+128°-cut LN crystals and a conventional bimorph soft PZT ceramic bonded to long spring-steel cantilevers as a function of the frequency, load resistance, and tip proof mass. At a low bending resonance frequency of ca. 32.2 Hz, the bidomain LN yielded an open-circuit voltage of 1.54 kV/g, almost one order of magnitude larger than that observed in PZT. The maximum extractable average power was found to be of 9.2 mW/g2 in the bidomain LN, 6.2 mW/g2 in the single-domain LN, and 1.8 mW/g2 in the PZT piezo-elastic cantilevers. With five times higher output power density of up to 11.0 mW/(cm [Formula: see text]) under resonance conditions, bidomain LN was thus shown to be a reliable lead-free and high-temperature alternative to PZT, thanks to its considerably larger quality factor and electromechanical conversion efficiency.